1.Polyester high tenacity yarn 500d,1000d,1300d,1500d,2000d,2500d,3000d,4000d….
Technical spec.:
Breaking Tenacity:9.1~9.30G/D
Breaking Elongation Ratio:14+/-2%
Hot Air Shrinkage(177Degree Celsius,10min.):6.5+/-1.5%
Packing::fixed weight 11 or 11.5 or 12 kgs/bobbin
Bobbin Dimension(without yarn)length-300mm, Inner dia.-94mm
2. Polyester HT Low shrinkage for sewing thread:50D/24F,70D/24F,100D/236F,
110D/36F,120D/36F,150D/48F,210D/60F,235D/60F,250D/60F&72F
300D/72F,420D/72F&120F,500D/96F&120F
Breaking tenacity:8+/-0.2G/D
Elongation at breaking:15+/-2%
Hot Air Shrinkage(177Degree Celsius,2min.,0.05cn/dtex):2.5+/-0.5%
Hot Air Shrinkage(177Degree Celsius,10min.,0.05cn/dtex):5+/-1%
Hot Air Shrinkage(130Degree Celsius,10min.,0.05cn/dtex):1.7+/-0.3%
Shrinkage after 95Degree Celsius cooking:0.6+/-0.1%
Packing:7.2~7.4kgs/bobbin,4bobbins/carton,
1x20FCL:12tons
1x40FCL:24tons
The height of paper bobbin:150mm.Inner diameter of paper bobbin:94mm,
External diameter of yarn:310mm
3. Technical spec. of HT Low Shrinkage Polyester Yarn1000D
Breaking Tenacity:>7.1Cn/Dtex
Breaking Elongation Ratio:22+/-2.0%
Hot Air Shrinkage(190Degree Celsius,15min.,0.01cn/dtex):3.5%
Hot Air Shrinkage(200Degree Celsius,15min.,0.01cn/dtex):3.9~4.0%
Packing::fixed weight 11 or 11.5 or 12 kgs/bobbin
Bobbin Dimension(without yarn)length-200mm, Inner dia.-94mm
4．Polyester Super low shrinkage yarn 1000D
Breaking Tenacity:>6.9Cn/Dtex
Breaking Elongation Ratio:23+/-2.0%
Hot Air Shrinkage(190Degree Celsius,15min.,0.01cn/dtex):2.3%
Packing::fixed weight 11 or 11.5 or 12 kgs/bobbin
Bobbin Dimension(without yarn)length-200mm, Inner dia.-94mm
5．Polyester dope dyed yarns 1000D,1500D,2000D,3000D
Technical spec. of dope dyed Polyester
Breaking Tenacity:8~8.5G/D
Breaking Elongation Ratio:11.5~13.5%
Hot Air Shrinkage(177Degree Celsius,1min.):6.0~8.5%
Packing::fixed weight 11 or 11.5 or 12 kgs/bobbin
Bobbin Dimension(without yarn)length-300mm, Inner dia.-94mm/112mm
6．Polyester twisted yarns
220D~500D~1000D~3000D~6000D~8000D Twist 18~666 Per Meter
Technical specifications
1）Linear Density:500D Twist Z or S 60~150 High Tenacity
1000D,1500D,2000D Twist Z or S 40~150 High Tenacity
Breaking Tenacity:>9.0G/D
Breaking Elongation Ratio:14.5+/-2.0%
Hot Air Shrinkage(170 Degree Celsius x 10Min):7%
(160 Degree Celsius x 15Min)<9.5%
2）.Linear Density:500D Twist Zor S 60~150 Low Shrinkage
Breaking Tenacity:>7G/D
Breaking Elongation Ratio:<23%
Hot Air Shrinkage(160 Degree Celsius x 15Min):<3%
3）.Linear Density: 1000D,2000D Twist Z or S 40~150 Low Shrinkage
Breaking Tenacity:>7.5G/D